Effect of Texture of Antireflection Layer on Photovoltaic Performance of Silicon/PEDOT:PSS Hybrid Solar Cells
Yuuki Sugano1, Keisuke Sato1*, Naoki Fukata2, Kenji Hirakuri1
Affiliation
- 1Department of Electrical and Electronic Engineering, Tokyo Denki University, Tokyo, Japan
- 2International Center for Materials Nanoarchitectonics, National Institute for Materials Science, Ibaraki, Japan
Corresponding Author
Keisuke Sato, Department of Electrical and Electronic Engineering, Tokyo Denki University, 5 Senju-Asahi-cho, Adachi-ku, Tokyo 120-8551, Japan, Tel: +81-3-5284-5406; E-mail: satok@mail.dendai.ac.jp
Citation
Sato, K., et al. Effect of Texture of Antireflection Layer on Photovoltaic Performance of Silicon/PEDOT:PSS Hybrid Solar Cells. (2017) J Nanotechnol Material Sci 4(1): 6- 13.
Copy rights
© 2017 Sato, K. This is an Open access article distributed under the terms of Creative
Commons Attribution 4.0 International License.
Keywords
Abstract
High-efficiency and low-cost silicon (Si)/organic hybrid solar cells have attracted significant attention as key devices to resolve global environmental problems, and also to enhance commercial usage. Herein, we report the correlation between the texture of the antireflection layer of hybrid solar cells composed of high-density textured Si and poly(3,4-ethylenedioxythiophene): poly(styrenesulfonate) (PEDOT: PSS) and their photovoltaic performance. The ‘micro-desert’ and ‘honeycomb’ textured configurations on the Si surface provide an excellent antireflection capability for the incident wavelength range of 500-1000 nm, endowing the cells with a remarkably low reflectance value below 11%. The photovoltaic performance is strongly influenced by the morphology of such an antireflection layer. In comparison with the honeycomb configuration hybrid solar cells, the micro-desert textured cells exhibit a good photovoltaic performance and a high power conversion efficiency of 5.43%, due to the uniform adhesion of the PEDOT:PSS layer on the textured surface and the effective collection of the separated charge carriers at the electrodes after a post-annealing process at 200°C. These findings contribute to technical knowledge for the development of highly efficient hybrid solar cells with an antireflection layer.